furnace carbon graphite electrodes 600mm with nipples
To control the quality of graphite electrodes, the following
measures are typically taken:
Raw material quality control: Strictly select high-quality graphite
raw materials and perform inspections and screenings on them.
Manufacturing process monitoring: Strictly monitor each process
step during manufacturing to ensure that process parameters meet
requirements.
Quality inspection: Perform various quality inspections on the
finished electrodes, such as resistivity testing, strength testing,
dimensional accuracy checks, etc.
Quality management system: Establish a comprehensive quality
management system to ensure the stability and consistency of
product quality.
In addition, manufacturers also provide customized graphite
electrode products based on customer needs and application
scenarios, along with related technical support and after-sales
service. Quality control is a crucial aspect of ensuring the
performance and reliability of graphite electrodes. Only through
strict quality control can high-quality graphite electrode products
be produced.
Product Parameters of Graphite Electrode
| RP | HP | UHP |
Electrode:
Bulk Density≥ 1.56g/cm3
Specific Resistivity≤ 8.5μm
Bending Strength≥ 10.0MPa
Elastic Modulus≤ 9.3GPa
Thermal Expansion Coefficient≤ 2.7x10 -6/°C
Ash≤ 0.5%
Nipple:
Bulk Density≥ 1.68g/cm3
Specific Resistivity≤ 7.0μm
Bending Strength≥ 14.0MPa
Elastic Modulus≤ 13.7GPa
Thermal Expansion Coefficient≤ 2.5 x10 -6/°C
Ash≤ 0.5% | Electrode:
Bulk Density≥ 1.65g/cm3
Specific Resistivity≤ 6.5μm
Bending Strength≥ 12.0MPa
Elastic Modulus≤ 10.0GPa
Thermal Expansion Coefficient≤ 2.2x10 -6/°C
Ash≤ 0.3%
Nipple:
Bulk Density≥ 1.74g/cm3
Specific Resistivity≤ 5.5μm
Bending Strength≥ 16.0MPa
Elastic Modulus≤ 14.0GPa
Thermal Expansion Coefficient≤ 2.0 x10 -6/°C
Ash≤ 0.3% | Electrode:
Bulk Density≥ 1.68g/cm3
Specific Resistivity≤ 5.8μm
Bending Strength≥ 16.0MPa
Elastic Modulus≤ 14.0GPa
Thermal Expansion Coefficient≤ 1.9x10 -6/°C
Ash≤ 0.2%
Nipple:
Bulk Density≥ 1.76g/cm3
Specific Resistivity≤ 4.5μm
Bending Strength≥ 18.0MPa
Elastic Modulus≤ 16.0GPa
Thermal Expansion Coefficient≤ 1.4 x10 -6/°C
Ash≤ 0.2% |
Packing & Delivery
REMARK: the above data is just on standard of YB/T, the actual
product is big different from the above. For the actual, be free to
contact us, please.
Service: We can supply you with free samples, a booklet, a
laboratory test report, an Industry Report, etc.
Welcome to our factory and company for a visit!
Company profile
ZHENAN has been in the business of ferroalloy for 3 years now. It
is a leading manufacturer and supplier of ferro silicon,silicon
manganese,silicon metal,silicon carbide,high carbon silicon and so
on.our company is a large-sized production enterprise integrating
research, development, production and sales.
Our company locates in Anyang city,Henan province of China a total
area of about 15,000 square.With many years growing and
developing,our company has domestic advanced smelting
furnaces,crushing and screening production lines with annual output
of 20000 tons.At the some time has two laboratories and a
metallurgical materials testing center with dozens of senior
researchers.The products are supplied to many large and
medium-sized iron and steel enterprises in China, and exported to
Japan, Korea, India, Europe and the United States.
RFQ
Q: Are you a manufacture or trader?
A: We are truly a manufacturer, we not only can provide the high
quality products with the best price, but also can offer the best
pre-sale service and after-service.
Q : What standards do you have?
A : Our products meet the standards, such as ASTM, ASME, AMS, DIN,
JIS etc.The third party testing is all available for us.
Q : What is your lead time?
A : It usually needs about 15- 20 days after receiving the PO.